Grade 201 stainless steel strip is a lower-cost alternative to the conventional Cr-Ni austenitic stainless steels, such as 304 strips.

Name: 201 Stainless Steel strip
SKU: 0

About half of the nickel content of 304 is replaced with alloy additions of manganese and nitrogen. This results in a higher strength than 304.

201 stainless steel strip has relatively lower ductility and formability compared to 301 stainless steel strip.

Grade 201 also has good welding characteristics and low temperature properties.

Specification

International Standard	ASTM/EN/JIS
Hardness	150-200HV
Thickness	0.03mm-3.0 mm
Width	1.5mm-600 mm
Edge	Mill Edge, Slit Edge, Deburred Edge, Round Edge, V Type Edge
Paper Core Internal Diameter	Ø500mm paper core, special internal diameter core and without paper core on customer request
Surface Finish	NO.1, 2B, 2H(Rerolled Bright), BA, No.4, 8K (Mirror), HL (Hairline), Polishing Bright, etc
Technical Treatment	Cold Rolled, Hot Rolled
Mill Test Certificate(MTC)	EN10204 3.1
Test Content	Flange & Flaring Test,Reverse Flattening Test, Roughness Test, Hydrostatic/Pneumatic Test, Eddy Current Test (NDT), Surface Finish Verification, Dimensional Inspection, Material Certification
Certificate	TUV ISO 9001:2015 , PED 2014/68/EU , AD 2000-WO DIN EN ISO 9606-1 , DIN EN ISO 14732 Welder Certificate EN ISO 9712 NDT Personnel Certificate EN ISO 15613 WPQR

GRADE	C	Si	Mn	P	S	Cr	Ni
201	≤0.15	≤1.00	≤7.50	≤0.060	≤0.030	16.00-18.00	3.50-5.50

Grade	Standard	Yield Strength Rp0.2(N/mm²)	Tensile Strength Rm(N/mm²)	Hardness(HR B)	Vickers Hardness(HV)	Elongation A50%
201	ASTM A240	≥275	≥520	Annealed	260	≥35